オートバイ用リアアームを想定したアルミニウム合金のフレッティング疲労強度改善のための表面処理に関する検討
西田 友久水谷 淳之介武藤 睦治松田 伸也川邑 正広二村 優
著者情報
ジャーナル フリー

2015 年 64 巻 11 号 p. 872-879

詳細
抄録

Plain fatigue and fretting fatigue strength tests of aluminum alloy (JIS A7N01) specimens with surface treatments (fine particle peening, burnishing and solid lubricant film) were carried out using an electromagnetic fatigue testing machine. Fretting fatigue limit of untreated specimen was significantly low, which was about one fourth of the plain fatigue strength. Fretting fatigue strength of the specimen surface-treated with fine particle peening was slightly higher than that of the untreated specimen. The fretting fatigue strengths for solid lubricant film and burnishing have been remarkably increased compared to that of the untreated specimen. However, the fatigue limit for solid lubricant film was almost same as that of untreated specimen. From the in-situ SEM observation of fretting fatigue process, it was found that burnishing with smooth surface and high compressive residual stress effectively delayed the fretting fatigue crack nucleation and crack propagation. It was also found that solid lubricant film with low frictional coefficient effectively delayed them.

著者関連情報
© 2015 日本材料学会
前の記事 次の記事
feedback
Top