Abstract
This paper is intended to develop and study the technology to produce the ceramics of cement mortar by using cement, fritted glaze, silica fume and some special sands. The specimens were casted (2×2×8cm) with this mortar. And after curing, they were fired at 940℃ or 1000℃ for two hours to measure the properties of these specimens before and after firing. As the result, the fritted graze of low fusing point with 20% frits/cement ratios and of 5〜8% silica fume/cement ratios was found to be most suitable for these ceramics of cement mortar. And the most suitable firing temperature for the properties of these specimens after firing is found to be 1000℃. And the surface of these mortar was tested to be colored with the glaze by these firing.