Fabrication of Ordered Poly[1,6-bis(3-nonyl-9-carbazolyl)-2,4-hexadiyne] Thin Film via Simple Spin-coating Process
Yuuki MiyazakiKazuo OkamotoKousuke TsuchiyaKenji Ogino
Author information
JOURNALS RESTRICTED ACCESS

2013 Volume 42 Issue 10 Pages 1217-1219

Details
Abstract

Diacetylene derivative, 1,6-bis(3-nonyl-9-carbazolyl)-2,4-hexadiyne was designed and synthesized. Compared with nonsubstituted 1,6-di(N-carbazolyl)-2,4-hexadiyne, the solubility was drastically improved, which allowed us the fabrication of a smooth crystalline thin film via a simple spin-coating process. The resulting film was easily polymerized by photoirradiation after thermal annealing. UV–vis absorption and Raman scattering spectra suggested topochemical polymerization. Out-of-plane XRD measurement of spin-coated film showed a strong diffraction. It suggests the interdigitation structure of alkyl chain. In-plane XRD measurements of spin-coated polymerized films showed two small peaks which were not identical to the result of out-of-plane XRD. These results indicated edge-on orientation. AFM image suggests that the film is composed of an aggregation consisting of needle-like nanostructures of polymer crystals.

Information related to the author

This article cannot obtain the latest cited-by information.

© 2013 The Chemical Society of Japan
Previous article Next article
feedback
Top