1999 Volume 67 Issue 12 Pages 1187-1188
The electrochemical properties of MoO3 on glassy carbon surface were evaluated. MoO3 was highly dispersed on glassy carbon surface when the loaded amount of MoO3 was 0.5 nmol cm−2. This electrode exhibited extremely high pseudocapacitance (118 kC mol−1), which is comparable to that of RuO2.