2001 Volume 69 Issue 8 Pages 612-614
Sintered ceramics Ca0.9La0.1MnO3−δ were studied on their properties as cathode active materials in some saline solutions. The ceramics were found to discharge without any conductive agents such as graphite in the neutral solutions, although the discharge capacity was lower than that in alkaline solution. The discharge capacity was the largest in 15% LiCl solution (188 mAh g−1).