2011 Volume 79 Issue 6 Pages 464-466
A performance at high temperature of all-solid-state battery with LiMn2O4/honeycomb Li0.35La0.55TiO3/Li4Mn5O12 configuration was examined. The charge and discharge capacities increased with test temperature until 100°C by favorable Li ion conductivity of electrolyte. At 120°C, deterioration of the performance was observed due to instability of electrode material. It is found that the all-solid-state battery can be operated until 100°C. The discharge capacity at 100°C was 74 µA h cm−2 at current density of 100 µA cm−2.