Conductivity of LiClO4/PC-DME Solution Impregnated in LiCoO2 Powder

Yoshimasa SUZUKI; Hideshi MAKI; Masaki MATSUI; Minoru MIZUHATA

doi:10.5796/electrochemistry.19-00044

Note

Conductivity of LiClO₄/PC-DME Solution Impregnated in LiCoO₂ Powder

Yoshimasa SUZUKI, Hideshi MAKI, Masaki MATSUI, Minoru MIZUHATA

著者情報

キーワード: Lithium Ion Battery, Ion Transport in Porous Electrode Materials, Binary Solvent

ジャーナルフリー
電子付録

2019 年 87 巻 5 号 p. 294-296

DOI https://doi.org/10.5796/electrochemistry.19-00044

Browse “Advance online publication” version

詳細

抄録

Electrical conductivity of LiClO₄ solution in binary solvent of propylene carbonate (PC) and 1,2-dimethoxyethane (DME) coexisting with LiCoO₂ powder was measured. Maximum value of conductivity in LiClO₄/PC-DME solution observed at ca. 1:1 of volume fraction shifted toward lower content of DME. In higher LiClO₄ concentration reached to 3 mol L⁻¹, the conductivity of LiClO₄-PC₁₋_xDME_x increased with DME content even if LiCoO₂ was added. The results of FT-IR measurement support the results of conductivity measurement for PC solvation of the slurry sample of LiCoO₂/LiClO₄/PC-DME system.