MOD法によるZrおよびNb添加VO₂薄膜の作製と特性評価

抄録

For the application of thermochromic smart windows, it is important to realize high visible light transparency, modulation of infrared transmission, and phase transition temperature around room temperature. For this purpose, vanadium dioxide (VO₂) thin films co-doped with niobium and zirconium were synthesized by metal-organic decomposition (MOD) method on glass substrates. First, the effect of Zr doping on the transparency of VO₂ thin films was investigated as a preliminary experiment. 3 mol% Zr doping improved the visible light transmittance of VO₂ thin films from 49% to 56%, and the phase transition temperature decreased from 81°C to 74°C without decreasing the switching ratio in the infrared region. Then, the effect of Zr and Nb co-doping on the transition temperature of VO₂ thin films was investigated. The VO₂ thin film co-doped with 3 mol% Zr and 4 mol% Nb could significantly decrease the phase transition temperature from 74°C to 48°C while nearly maintaining the visible light transmittance.