Regular Article
Behavior of Phosphorous Transfer from CaO–FetO–P2O5(–SiO2) Slag to CaO Particles
Hideaki SuitoRyo Inoue
Author information

2006 Volume 46 Issue 2 Pages 180-187


Lime particles (0.5 to 1 mm) were added by dropping to CaO–FetO–P2O5 slag at 1 400°C, followed by stirring and the reaction products near a CaO particle/slag interface were determined by a microprobe analysis (EPMA-EDX). The 3CaO·P2O5 and 4CaO·P2O5 phases were crystallized depending on the amount of added CaO particles which are rapidly dissolved after the contact with a molten slag. The phosphorous distribution ratios between calcium phosphates and CaO–FetO slag obtained at temperatures between 1 400 and 1 570°C are higher than those between 2CaO·SiO2–3CaO·P2O5 solid solution and CaO–SiO2–FetO slag. Lime particles (0.3 to 0.5 mm) are added to CaO–SiO2–FetO–P2O5 slag at 1 400°C and the reaction products near a CaO particle/slag interface are determined by EPMA-EDX. The 2CaO·SiO2–3CaO·P2O5 solid solution layer is formed on the surface of a CaO particle and thereafter the CaO–FetO slag layer is formed between a CaO particle and 2CaO·SiO2–3CaO·P2O5 solid solution layer which is surrounded by CaO–SiO2–FetO–P2O5 slag. It is also experimentally confirmed that the meso-phase slag refining is superior to conventional slag refining and the discrepancy between the theoretical and experimental results obtained by the meso-phase slag refining is discussed.

Information related to the author
© 2006 by The Iron and Steel Institute of Japan
Previous article Next article