Grain Refinement and Improvement in Mechanical Properties of Nb–Al–Si Intermetallic Alloys
Kiyotaka MatsuuraDariusz Boleslaw KataJerzy Tadeusz LisMasayuki Kudoh
Author information
JOURNALS FREE ACCESS

2006 Volume 46 Issue 6 Pages 875-879

Details
Abstract

Nb–Al–Si intermetallic alloys having submicron crystal grains have been produced using the self-propagating high-temperature synthesis (SHS, or combustion synthesis) method followed by the bead milling technique and the spark plasma sintering (SPS) method. The intermetallic alloys were combustion-synthesized from elemental powders of niobium, aluminum and silicon, and then ball-milled and bead-milled to reduce the alloy powder particle size. The milled alloy powder was consolidated using the SPS method with a sintering time of 300 s at a sintering temperature of 1 373 K. The increase in milling time reduced the grain size of the sintered alloy. Particularly, the grain size was dramatically reduced when zirconia beads of a 0.2-mm diameter were used after milling with zirconia balls of a 10-mm diameter. The Vickers hardness, bending strength and fracture toughness of the sintered alloys increased with the decrease in grain size.

Information related to the author
© 2006 by The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top