Interaction between Steel and Distinct Gunning Materials in the Tundish
Pengcheng YanMarie-Aline Van EndeEnno ZinngrebeSieger van der LaanBart BlanpainMuxing Guo
Author information
JOURNALS OPEN ACCESS FULL-TEXT HTML

2014 Volume 54 Issue 11 Pages 2551-2558

Details
Abstract

Gunning materials are used as a dispensable protective layer to extend the tundish life. Their use however, affects the steel cleanliness by introducing steel reoxidation and exogenous inclusions. In the present work, the interaction between molten steel and three types of refractory, i.e. MgO, Al2O3, and MgO + 2MgO∙SiO2 based gunning materials (GM) have been investigated. Compared to MgO and MgO + 2MgO∙SiO2 GM, the Al2O3 GM exhibited better infiltration resistance to molten steel. The two phase MgO + 2MgO∙SiO2 GM was found to be less prone to steel infiltration than single-phase MgO GM. The compositional evolution of steel influenced by gunning material was experimentally measured and also predicted with thermodynamic equilibrium calculations. The steel cleanliness in terms of inclusion size, number density, area fraction and morphology was measured and evaluated. Although large Al2O3/AlTiOX inclusions were formed through the erosion of Al2O3 GM, the use of Al2O3 GM resulted in an improved steel cleanliness due to its lower content of reducible compounds compared to that of MgO and MgO + 2MgO∙SiO2 GM.

Information related to the author
© 2014 by The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top