Comparison of Hydrogen Embrittlement Resistance of High Strength Steel Sheets Evaluated by Several Methods
Shusaku TakagiYukito HagiharaTomohiko HojoWataru UrushiharaKaoru Kawasaki
Author information

2016 Volume 56 Issue 4 Pages 685-692


Applications of ultra-high strength steel sheets to automotive bodies have expanded steadily in recent years. Various methods are used to evaluate resistance to hydrogen embrittlement (HE), which is one problem of ultra-high strength steels. In this study, the critical HE conditions obtained by the SSRT, CSRT and 4-point bending test were compared by using the same materials. The materials were two ultra-high strength steel sheets with tempered martensite microstructures, one with the SCM435 composition and the other a V-added steel containing many hydrogen trapping precipitations. The specimens were charged with hydrogen by the cathodic charging method. The specimens used in the SSRT and CSRT were machined with notches on both sides of the parallel part. The values of the stress concentration factor (Kt) of the specimens were 4.26 and 1.76. A coupon-shaped specimen was used in the 4-point bending test. The critical HE conditions evaluated by the average applied stress and the average hydrogen content of the specimen were different depending on the test methods. The HE conditions were also evaluated by the local stress and the local accumulated diffusible hydrogen content at the fracture initiation point. The critical condition evaluated by the 4-point bending test was located in a higher stress and higher hydrogen content region compared with the critical conditions obtained by the CSRT and the SSRT.

Fullsize Image
Information related to the author
© 2016 by The Iron and Steel Institute of Japan
Previous article Next article