Quantitative Evaluation of Reaction Mode and Reduction Disintegration Behavior of Iron Ore Agglomerates during Low Temperature Reduction
Moritoshi MizutaniTsunehisa NishimuraTakashi OrimotoKenichi HiguchiSeiji NomuraKoji SaitoEiki Kasai
Author information

2018 Volume 58 Issue 10 Pages 1761-1767


The utilization of H2 in the ironmaking process is a potential option for a further reduction of CO2 emission from the blast furnace (BF). H2 promotes the reduction reaction of burden materials, but its influence on their reduction disintegration behavior remains unknown in detail. This study investigates its influence on the specified essential factors governing the reduction disintegration behavior of the iron ore agglomerates, i.e., iron ore sinters and pellets.

Reduction disintegration index (RDI) values were measured after the reduction of the agglomerate samples using the gas mixtures of CO–H2–CO2–N2. The mineral textures of reduced samples were observed using an optical-microscope and an electron probe micro-analyzer for the evaluation of reaction modes. Further, Thiele modulus (ϕ), which is considered as the index of reaction modes during reduction, was calculated using the measurement results. The calculated ϕ showed reasonable correlation with RMI values, which is one index of the reaction mode evaluated by an elemental analysis using EPMA. Disintegration does not make much progress when ϕ is larger than a certain limit value, whereas it proceeds significantly when ϕ is less than that value.