Degradation Behavior of Coke Reacting with H2O and CO2 at High Temperature
Ping WangYue-qiang ZhangHong-ming LongRu-fei WeiJia-xin LiQing-min MengShu-cai Yu
Author information
JOURNALS OPEN ACCESS Advance online publication

Article ID: ISIJINT-2016-488


The degradation behaviors of coke which reacts with CO2 and H2O were explored in self-made gas-solid reacting apparatus. It was observed that the temperature loss of coke with H2O in initial and violent solution were about 37°C and 125°C lower than that with CO2 respectively. The gasification rate of coke with H2O was about 1.27–3.16 times faster than that with CO2. But the difference of gasification rate will reduce with the lower temperature. The coke strength after reaction (CSR) with H2O was lower than with CO2 at 950°C–1100°C, but higher at 1200°C. The coke's apparent porosity and changing rate after reacting were both smaller with H2O than with CO2. It is mainly due to the reaction that occurred closer to the coke particle surface with H2O than with CO2.

Information related to the author
© 2017 by The Iron and Steel Institute of Japan