Precipitation and Growth of γ' and η Phases in 53Fe-26Ni-15Cr Alloy
Kiyoshi KusabirakiYushin TakasawaTakayuki Ooka
Author information
JOURNAL FREE ACCESS

1995 Volume 35 Issue 5 Pages 542-547

Details
Abstract

The nucleation and growth behavior of γ' and η precipitates in A286 alloy was investigated by micro-Vickers hardness test and transmission electron microscopy. The morphology and the crystallography of them were also discussed. The hardness of A286 aged at 893-1073 K for durations up to 720 ks was closely related to the mean size of γ' precipitates. The growth kinetic of the γ' precipitate in η-phase free region was explained by Lifshitz-Slyozov-Wagner's theory for diffusion controlled growth at 993-1073 K. The activation energy for the growth of the γ' precipitates was estimated to be 283 kJ/mol.