1996 Volume 36 Issue 5 Pages 512-516
Ferrous oxide activity has been determined in molten synthetic slag mixtures of the quaternary system FeO-TiO2-CaO-Al2O3 at constant levels of Al2O3. Furthermore, in the course of determining the FeO activity in this quaternary system, the ternary system FeO-CaO-Al2O3 was also investigated at 1450°C.
The technique used to measure the ferrous oxide activity in the investigated systems was the well established one of gas-slag-metal equilibration in which molten slags contained in armco iron crucibles are exposed to a flowing gas mixture with a known oxygen potential until equilibrium has been attained. After equilibration, the final chemical analysis of the slags give compositions having a particular ferrous oxide activity corresponding to the oxygen potential of the gas mixture.
The effect of Al2O3 additions on the FeO activity was determined. The results are presented as a series of iso-activity curves on pseudo-ternary diagrams. The interdependence between the ferrous oxide activities and slag composition was also studied.