Nb-doped SrTiO3 多結晶体の熱電特性の粒径依存性
太田 慎吾太田 裕道河本 邦仁
著者情報
ジャーナル フリー

114 巻 (2006) 1325 号 p. 102-105

詳細
PDFをダウンロード (341K) 発行機関連絡先
抄録

We investigated thermoelectric properties of 20-%-Nb-doped SrTiO3 at high-temperature (300-1000 K) using single-crystalline epitaxial film, polycrystalline film (average grain size ~200 nm) and ceramic (average grain size ~20 μm) samples to clarify the effect of grain boundaries on the thermoelectric performance. Although carrier concentration and Seebeck coefficient of all samples showed no significant differences, Hall mobility of the polycrystalline film was extremely small («10-1 cm2V-1s-1 at 300 K) as compared to those of the epitaxial film and the ceramic sample (~3 cm2V-1s-1). However, it drastically increased with increasing temperature and exhibited the value similar to those of the epitaxial film and the ceramic sample above 700 K. The thermoelectric figure of merit for 20%-Nb-doped SrTiO3 was found to reach 0.35 at 1000 K irrespective of the grain size.

著者関連情報
© 2006 The Ceramic Society of Japan
前の記事 次の記事
feedback
Top