抄録
Silicon carbide (SiC) powder was prepared by heating a mixture of fullerene and silicon powders at 900-1000 K for 24 h with a Na flux. X-ray and electron diffraction revealed that the obtained powder was β-SiC. The agglomerates of SiC particles with a size of a few dozen nm were observed by transmission electron microscopy. The specific surface area and mean particle size of the SiC powder prepared at 1000 K were 12 m2/g and 88 nm, respectively.