Abstract
The influence of alloying elements on the precipitation behavior of sigma (σ) phase was investigated for conventional SAF2205 and SAF2507 super duplex stainless steel. Time-Temperature-Precipitation (T-T-P) diagram of sigma phase of SAF2507 were shifted toward to shorter times compared to SAF2205. The precipitation of sigma phase was accelerated with increasing Cr and Mo concentration. According to the microstructure observation, the sigma phase began to precipitate at ferrite (α) ⁄ austenite (γ) phase boundaries and grew into ferrite for SAF2507 and SAF2205 steel. In the as-received condition, Cr and Mo concentration in ferrite was clearly higher than that in austenite. Especially, it was found that Mo concentration in ferrite of SAF2507 was higher than that in ferrite of SAF2205. The result of EPMA-measurement showed that sigma phase was mainly Fe-Cr-Mo intermetallic compound and Mo was significantly enriched into sigma phase. The difference of Mo concentration in ferrite significantly affected to the sigma phase precipitation. The secondary austenite formation was also induced by sigma phase precipitation. Cr and Mo were ejected to the remained ferrite ⁄ austenite phase boundaries by secondary austenite formation. Consequently, sigma phase precipitation was more accelerated by the reheating.