フェムト秒レーザ照射による酸化チタン膜の光触媒機能変化
塚本 雅裕篠永 東吾堀口 直人吉田 実藤田 雅之阿部 信行
著者情報
ジャーナル フリー

2011 年 37 巻 6 号 p. 311-315

詳細
抄録

  Titanium dioxide (TiO2) is functional ceramics and shows the photocatalytic function by ultraviolet light illumination. This photocatalytic function enables decomposition of organic matter such as bacteria, mold and odors. In our previous study, the TiO2 film was darkened by the femtosecond laser irradiation and electrical resistance of the darkened film was decreased. In this study, we investigated variation of the photocatalytic function of the darkened TiO2 films. The TiO2 film was produced by aerosol beam irradiation. The wavelength, the pulse width and the repetition rate of the femtosecond laser were 775 nm, 150 fs and 1 kHz, respectively. The laser spot was scanned on the whole area of the TiO2 film surface and the laser fluence was changed within the laser fluence regime in which the laser ablation was not caused and topography of the film surface was not varied. The photocatalytic function of the darkened TiO2 films was evaluated in the acetaldehyde decomposition test. In the test, the films in acetaldehyde were illuminated with the UV and visible light sources, respectively. The acetaldehyde concentration was measured every hour during the illumination. The results of the test shows that the film had photocatalytic function by visible light illumination.

著者関連情報
© 2011 (社)高温学会
前の記事 次の記事
feedback
Top