硫酸塩浴からの亜鉛-ポリエチレンイミン複合電析挙動とその微細構造
渕 浩輔大上 悟菊池 義治赤松 慎也柏 裕樹中野 博昭
著者情報
ジャーナル フリー HTML

2018 年 82 巻 8 号 p. 281-288

詳細
抄録

Electrodeposition of Zn-polyethyleneimine composite was performed at current density of 100-12000 A·m-2 and a charge of 4.8×105 C·m-2 in an agitated sulfate solution containing 1.84 mol·dm-3 of ZnSO4 and 4 g·dm-3 of polyethyleneimine at pH 1.8 and at 313 K, and the deposition behavior and its micro structure were investigated. The films deposited at current densities above 4000 A・m-2 from the solution containing polyethyleneimine exhibited the gloss, and the gloss was highest with polyethyleneimine of higher molecular weight of 70000. The preferred orientation of deposited Zn changed from {0001} to {1120} and {1010} with polyethyleneimine, and the size of Zn platelet crystals deceased with increasing the molecular weight of polyethyleneimine and current density. The deposition of Zn was polarized with polyethyleneimine, and the degree of polarization became larger at higher current density region with polyethyleneimine of higher molecular weight of 70000. With increasing the molecular weight of polyethyleneimine and current density, the content of C and N in deposited films increased, indicating the increase in adsorption ability of polyethyleneimine onto cathode. Polyethyleneimine somewhat suppressed the rise of pH at cathode layer during deposition, or showed the buffer action of pH. During deposition, H+ ions are detached from the polyethyleneimine due to rise of pH at cathode layer and, as a result, the lone pairs of electron in N atom increased, which resulted in increase in adsorption ability of polyethyleneimine onto cathode.

著者関連情報
© 2018 (公社)日本金属学会
前の記事 次の記事
feedback
Top