Abstract
High speed steel specimens were worked by torsion at the temperature of 1000∼1200°, and austenite grain-growth was observed with microscope. Austenite grain-boundaries were revealed by keeping the specimens at 800° for 10 minutes, the temperature bringing the nose in S curve. The outlines of the experiments are as follows :
\
oindent(1) The relation between the degree of deformation, grain size and the working temperature was measured.
\
oindent(2) The progress of recrystallization or grain-growth with the lapse of time after hot working was observed.
\
oindent(3) The relation between the degree of deformation and the lapse of time before recrystallizing was found out.
\
oindent(4) It was observed that the successive alternating working diminished the capacity of recrystallization.
\
oindent(5) Coarse austenite grains were incapable of being recovered by the heat treatment.