1990 年 14 巻 2 号 p. 189-192
Melt-spun ribbons and sintered materials with the composition of Nd15(Fe1-x-yCoxNiy)77B8 were investigated with respect to saturation magnetization, coercivity, Curie temperature and corrosion characteristics. It was found that double substitutions of Co and Ni atoms for Fe atoms enhance the intrinsic coercivity of sintered magnets for compositions of 0.2≤x≤0.4 and 0.0≤y≤0.2, and improve corrosion resistance. A further addition of Ti atoms to the system increases the coercivity and makes the demagnetization curve rectangular. For example, (BH)max and intrinsic coercivity in Nd15(Fe0.585Co0.30- Ni0.10Ti0.015)77B8 amount to 33.8 MGOe and 10.4 kOe, respectively.