ランダム化処理したFe-4 at% Cr-10 at% Si-15 at% Bの高耐食性
1997 年 9 巻 1-2 号 p. 76-78
詳細
1997 年 9 巻 1-2 号 p. 76-78
The present study has been initiated to observe the effect of randomization on a passivity-maintaining current density (Ip) in anodic polarization curve in a liquid-quenched Fe-4 at% Cr-10 at% Si-15 at% B alloy glass. The randomization decreases both a passivity current density and passivity-maintaining current density, thus improving the corrosion resistance of the glassy alloy.