クリープき裂伝ぱを支配する破壊力学的因子

抄録

A critical examination was made on the applicability of fracture mechanics parameters to crack propagation under creep condition in 304 stainless steels with a wide variety of specimen geometries at a high stress level. The creep crack propagation rate could not be described in terms of elastic stress intensity factor but it could be in terms of net section stress for all dimensions of thin plate specimens. The net section stress, however, could net explain the difference between the crack propagation rates of thin plate specimens and those of notched round bar specimens. This difference could be ascribed to the plastic constraint around the crack tip. Applicability of the modified J integral to creep crack propagation was also examined and the results showed that this parameter was the best one to predict the creep crack propagation rate at high stress level. In the case of specimens of similar geometries, the net section stress could be used in place of the modified J integral provided that the crack propagation rate was divided by the characteristic length of the specimen.