高温におけるSUS304ステンレス鋼の Fast-Fast 型疲労き裂の進展挙動に及ぼす1サイクルの Slow-Fast ひずみの導入の影響
岡崎 正和服部 一郎小泉 堯
著者情報
ジャーナル フリー

1984 年 33 巻 373 号 p. 1285-1291

詳細
抄録

The fatigue crack growth behavior of SUS 304 stainless steel when one slow-fast strain cycle was introduced to the fast-fast strain cycles was investigated at the temperature of 873K. It was found that the fatigue crack growth rate in the fast-fast strain cycles was accelerated by the introduction of one slow-fast strain cycle. It was also found that there was a linear relationship between the size of the region where the above acceleration occurred and the value of creep J-integral range which was produced just when one slow-fast strain cycle was introduced. The distribution of hardness just below the fracture surface, where the above acceleration occurred, was similar to the one in the pure slow-fast strain cycle fatigue. From the results thus obtained, it was thought that the one slow-fast strain cycle affected the stress-strain field at the crack tip and contributed to the acceleration of crack growth rate.

著者関連情報
© 日本材料学会
前の記事 次の記事
feedback
Top