2004 Volume 45 Issue 8 Pages 2780-2784
The martensitic transformation and magnetic properties of Cu-Ga-Mn β alloys were investigated. The alloys in the composition range Cu-21 at%Ga-(13—15)at%Mn were found to exhibit a thermoelastic martensitic transformation from an L21 parent to a 2H martensite in the ferromagnetic state. This martensitic transformation disappeared with the precipitation of the ω phase induced by aging at room temperature.