Effects of Shielding Gas Flow Rate and Power Waveform on Nd:YAG Laser Welding of A5754-O Aluminum Alloy
Tsung-Yuan KuoYen-Tsun Lin
Author information

2006 Volume 47 Issue 5 Pages 1365-1373


Although the microstructure, hot crack susceptibility and porosity of aluminum alloy laser welds are affected by many welding parameters, the effects of the shielding gas flow rate and the power waveform are particularly significant. In this study, a high-power Nd:YAG laser is used to weld A5754-O aluminum alloy sheets of 1 mm in thickness. Initially, bead-on-plate (BOP) welding is performed using a rectangular waveform with a constant mean output power and three different levels of ΔPP=PpPb, where Pp is the peak power and Pb is the base power). Butt welding is then performed using the appropriate BOP welding speed, which is lower than the welding speed for just full penetration, and one of two levels of ΔFF=FfFb, where Ff is the face shielding gas flow rate and Fb is the back shielding gas flow rate). The BOP welding results show that reducing the value of ΔP increases the welding speed required for full-penetration, and therefore increases the penetration depth to bead width ratio and the micro-hardness of the weld bead. The butt welding results show that the tensile strength and total elongation properties of the high ΔFFH) specimens are approximately three times higher than those of the low ΔFFL) specimens. This is primarily due to the absence of hot cracking in the ΔFH specimens, together with a finer microstructure and a lower level of porosity. This study demonstrates that the effect of ΔF on the weld bead geometry, microstructure, hot crack susceptibility and mechanical properties is far higher than that of ΔP. However, the effect of ΔP on the change of welding speed is higher than that of ΔF.

Related papers from these authors
© 2006 The Japan Institute of Metals and Materials
Previous article Next article