Evolution of Microstructural Banding during the Manufacturing Process of Dual Phase Steels
Francisca G. CaballeroAndrea García-JuncedaCarlos CapdevilaCarlos García de Andrés
Author information

2006 Volume 47 Issue 9 Pages 2269-2276


The segregation of manganese during solidification from casting is responsible for banding problems of dual phase steels. Microstructural banding lasts during all the manufacture process, producing the deterioration of the material, so the final ductility and impact toughness of the sheets are decreased due to the high level of anisotropy. To avoid or reduce the problem of microstructural banding, it is proposed to modify the hot rolling parameters so the formation of ferrite-pearlite microstructures is avoided and thus the presence of banding. The study of the microstructural evolution during the whole manufacturing process reveals that the increase of the cooling rate during the hot rolling leads to a significant decrease of martensite banding in the microstructure of dual phase steels for sheets used in the automotive industry.

Information related to the author
© 2006 The Japan Institute of Metals and Materials
Previous article Next article