2007 Volume 48 Issue 7 Pages 1822-1827
The hydrogen internal friction peak in Zr50-metallic glasses (Zr50Cu50, Zr50Cu40Al10 and Zr50Cu35Al10Ni5) was studied. The hydrogen internal friction peak was shifted exponentially to lower temperatures with increasing hydrogen concentration similarly to other Zr-Cu base metallic glasses reported in the literature. The peak height increased in proportion to the square-root of hydrogen concentration. These results were discussed in the view point of the hydrogen induced structural relaxation in these metallic glasses.