Structural and Optical Characteristics of BaTiO3:Yb3+ Powders
A. García MurilloF. J. Carrillo RomoM. García HernándezO. Barbosa GarcíaA. Meneses NavaS. Palomares SánchezA. Flores Vela
Author information

2009 Volume 50 Issue 7 Pages 1850-1854


Yb3+ doped Barium Titanate powders were prepared by the sol-gel method in order to study their structural and luminescent properties. These powders have potential to be used to prepare films for luminescent screens. The synthesized powders were obtained at 2, 4 and 8% mol Yb3+ doped BaTiO3. In order to determine organic compound decomposition, weight loss, and establish the crystallization process, we performed TGA and DTA analyses. The powders were also thermally treated at temperatures ranging from 700 to 1200°C in order to study the structure evolution. Pure doped BaTiO3 powders were carefully studied by X-ray diffraction (XRD). Observations of the powders using scanning electron microscopy (SEM) were done in order to correlate the grain size with the luminescent properties. A comparative study of the spectroscopy properties constituted by emission, absorption spectra, and fluorescence decay measurements using NIR excitation were done. The Yb3+ ions pairs emission was measured in the green region at about 500 nm when pumping at 940 nm.

Information related to the author
© 2009 The Japan Institute of Metals and Materials
Previous article Next article