2010 Volume 51 Issue 1 Pages 78-84
Zincate treatment and electroless nickel-phosphorus plating for aluminum alloys of A1100, A2017, A5052 and A7075 were researched from the viewpoints of alloying elements and activation conducted prior to zincate treatment. Surface morphologies of zincated surfaces, electrochemical properties during zincate treatment and depth profiles on activated and zincated surfaces were investigated by microscopy and measurement of temporal changes of electrode potential.
Adhesion strengths of the plated films were measured by 90° peeling test, which showed that double zincate treatment improved adhesion strength especially when ferric ion was added into the zincate solution except for the case of A7075. Temporal changes of electrode potential during zincate treatments and morphologies of the zincated surfaces showed that copper and zinc promoted uniform precipitation of zinc and resulting rapid termination of conversion reaction. Excess zinc was shown to dissolve into the plating solution and cause the formation of low-density area or gaps between plated films and substrates.
Activation for A1100 by various conditions showed that formation of oxide film had a remarkable effect on precipitation of zinc during zincate treatment. When a mixture of nitric and hydrofluoric acid was used for activation, finer particles of zinc were formed near etch pits compared with the cases of hydrochloric or nitric acid. On the other hand, the surface was uniformly covered with fine zinc particles in the case of the activation with a solution of sodium hydroxide. This indicates that uniformity of oxide film on substrate before zincate treatment is thought to bring about uniform precipitation of zinc.