2010 Volume 51 Issue 3 Pages 525-528
Shape memory response of the polycrystalline Ni40Co10Mn33Al17 alloy were investigated. In the isobaric thermal cycling experiments, the measured transformation strain levels increased with increasing stress reaching about 3.6% under 200 MPa. The slope of the stress vs. transformation temperature diagram, constructed using the data from these experiments, almost coincided with the predicted one obtained using the Clausius-Clapeyron equation, and experimental entropy data and transformation strain. Perfect pseudoelasticity was observed up to 405 K during compressive straining up to 2.5%.