Effect of Annealing Temperature on Microstructure and Superelastic Properties of Ti-Au-Cr-Zr Alloy
Yuri ShinoharaMasaki TaharaTomonari InamuraShuichi MiyazakiHideki Hosoda
著者情報
ジャーナル フリー

2015 年 56 巻 3 号 p. 404-409

詳細
抄録

Effect of annealing temperature on microstructure and superelasticity of Ti-4Au-5Cr-8Zr (mol%) was investigated. Only β phase was observed in the specimen annealed at 1173 K, whereas the precipitation of Ti3Au, Zr33Ti40Au27 (Laves phase) and α phase occurred in the specimens annealed below 1073 K. Superelasticity was clearly observed in the specimens annealed at 1073 K and 1173 K, though it was absent in the specimens annealed at 873 K and 973 K. The maximum superelastic recovery strain was increased by the precipitation of Ti3Au in the specimen annealed at 1073 K. This is due to the increase in the critical stress for slip by the precipitation strengthening effect of Ti3Au.

著者関連情報
© 2015 The Japan Institute of Metals and Materials
前の記事 次の記事
feedback
Top