Characterization of Al/Ti Nano Multilayer as a Jointing Material at the Interface between Cu and Al2O3
Jianglong. YiYupeng ZhangXinxin WangChunlin DongHaichun Hu
Author information

2016 Volume 57 Issue 9 Pages 1494-1497


In this paper, a series of Al/Ti multilayers with different modulation periods were used in copper and Al2O3 ceramic diffusion bonding. The reactive multilayer was deposited by DC magnetron sputtering, and the diffusion bonding experiments were performed at 900℃ for 10 min with a pressure of 5 MPa. The interfacial joints were inspected by scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDS), X-ray diffraction and tensile shear tests. As a result, no significant metallurgical defect was observed in the microstructures of the joints. The formation of several intermetallic compounds at the interface, such as Cu/Ti eutectic and Al2O3-X·TiO compound, has further confirmed the success of Cu-Al2O3 bonding as compared to the Al/Ni nano-multilayers, which use Al/Ti nano-foils as interlayer for diffusion bonding to bring more benefit to the quality of cermet joint.

Information related to the author
© 2016 The Japan Institute of Metals and Materials
Previous article Next article