Corrosion Resistance of New Copper Alloy Castings Registered in JIS H 5120:2016 Copper Alloy Castings
Hiroshi YamadaMasaaki YamamotoToshimitsu OkaneYoshiharu KousakaYoshiyuki GotoTomoki Ito
Author information

2017 Volume 58 Issue 8 Pages 1169-1174


Four kinds of dezincification corrosion resistance brass casting (JIS symbols CAC211, CAC221, CAC231 and CAC232) and two kinds of Bismuth bronze castings (JIS symbols CAC905 and CAC906) were suggested to Japanese Industrial Standards (JIS H2210, H5120 and H5121) as alloys applicable to tools related to water supply appliances. For the corrosion-resistant evaluation of those six new alloys (registered new materials), dezincification-corrosion test (ISO 6509-1981), erosion-corrosion test (jet-in-slit test) and stress-corrosion-cracking test were carried out, and the results were compared with JIS copper alloys (CAC203, CAC804, CAC902 and C3771). The dezincification corrosion resistance of the registered materials was better than CAC203 and equal to CAC804 and CAC902. In the erosion-corrosion test of the JIS copper alloys, CAC902 was excellent, followed by CAC804, C3771, and CAC203 (CAC902 >> CAC804 > CAC3771 > CAC203) in this order. Among the registered alloys, CAC211, CAC231, CAC905 and CAC906 showed good erosion-corrosion resistance equal to CAC902. The erosion-corrosion resistance of CAC221 and CAC232 was worse than CAC902 and equal or slightly better than CAC804. In addition, it was revealed that the erosion-corrosion resistance improved when tin was contained. In the stress-corrosion-cracking test, the stress-corrosion-cracking sensitivity of the registered materials was lower than C3771 and CAC203.


This Paper was Originally Published in Japanese in J. JFS 87 (2015) 830–835.

Information related to the author
© 2017 Japan Foundry Engineering Society
Previous article Next article