Effective Alloying Treatment for Platinum Using Iron Chloride Vapor
Yu-ki TaninouchiToru H. Okabe
Author information

2018 Volume 59 Issue 1 Pages 88-97


An effective alloying treatment for Pt using FeClx (x = 2, 3) vapor was demonstrated towards developing a novel recovery process for platinum group metals (PGMs) in catalyst scrap. Suitable reaction conditions were discussed from the perspective of thermodynamics, and its validity was confirmed experimentally. When pure Pt samples were reacted with FeCl2 vapor at 1200 K under the coexistence of metallic Fe, an Fe-Pt alloy showing ferromagnetism was easily formed, even though the samples were not in physical contact with the metallic Fe. On the basis of thermodynamic considerations, alloying of Pt mainly proceeds via the disproportionation of FeCl2 vapor, with the gaseous phase containing FeClx acting as the medium to transport Fe from the metallic Fe to the Pt samples. When the alloyed sample was kept under FeCl3 vapor at 1200 K, Fe was removed and ferromagnetism was lost. Therefore, it is concluded that FeCl2 vapor treatment under the coexistence of Fe is a feasible and useful technique for alloying Pt and forming a ferromagnetic Fe-Pt alloy. The results obtained in this study indicate that treatment with FeCl2 vapor followed by magnetic separation has potential as an effective technique for concentrating PGMs directly from catalyst scrap.

Fig. 1 Schematic illustration of alloying treatment using FeClx (x = 2, 3) vapor. After the alloying treatment, PGMs can be effectively concentrated by magnetic separation. Fullsize Image
Information related to the author
© 2017 The Mining and Materials Processing Institute of Japan
Previous article Next article