Article ID: M2017270
Characteristic property changes were observed for high density and high purity nanocrystalline (n-) Au prepared by the gas deposition method. The increase in internal friction with a modulus defect started at ~180 K and became steep above 200 K. An increase in endothermic heat flow began at ~170 K. The electrical resistivity showed a deviation from a linear increase with the temperature at ~130 K. All the characteristic changes were reproduced by the repetition of the thermal cycle below 300 K, but the amounts diminished after the grain growth. These characteristic temperature changes indicate a glass-transition-like behavior of the grain boundaries in n-Au.