2005 年 12 巻 316 号 p. 179-183
This paper discusses the hydration products in C3A-CaSO4.2H2O-CaCra4system. The mole ratio of gypsum to C3A is 2/3 and the replacement mole ratio of CaCrO4 to gypsum is ranged from 0 to 1.0. CrO42- is fixed to AFm phase and the basal space of AFm is not changed until the replacement ratio of CaCrO4 is 0.25. But, the basal space of AFm is increased and the XRD peak of AFm become broad with increasing of the replacement ratio of CaCrO4. In CrO42--AFm, the basal space changed from 0.98 into 1.02 nm depending on a synthetic condition and the drying conditions, and the water between layers in AFm in that case was presumed to be 12 and 14 moles.