1990 Volume 66 Issue 10 Pages 193-196
A time-of-flight neutron diffraction experiment was undertaken on a powder sample of orthorhombic ZrO2 synthesized at 600°C and 6GPa for 30min. The Rietveld analysis for the diffraction data shows that the space group of this phase is Pbca. The refined lattice parameters are a0=1.00861, b0=0.52615, and c0=0.50910nm.