Nb含有フェライト系ステンレス鋼JFE429EX溶接継手の大気中および塩水中における疲労挙動に及ぼす溶接金属の影響
秋田 正之柿内 利文小山 敦弘中島 正貴高瀬 徹縣 幸男竹尾 友佑今里 周平杉本 大志植松 美彦
著者情報
ジャーナル フリー

2018 年 36 巻 4 号 p. 238-246

詳細
抄録

Effect of weld metals on the fatigue behavior of Nb-added ferritic stainless steel JFE429EX (15Cr-0.9Si-0.5Nb) welds in laboratory air and in 3% NaCl solution was investigated. Two filler metals with different chemical compositions, Filler I and II, had been used for the MIG butt welding of JFE429EX. Filler II contains Al and Ti to improve microstructure of fusion zone (FZ), resulting in the finer grains than Filler I. Fully reversed axial fatigue tests had been performed using smooth specimens of welds and base-metal specimens at ambient temperature in laboratory air and in 3% NaCl solution. In laboratory air, fatigue strengths of the welds with Filler II were higher than those of the base metal and welds with Filler I. Fatigue fracture occurred at HAZ and FZ in the welds with Filler I, while at base metal in the welds with Filler II. It could be attributed to the finer grains in the FZ of Filler II. In 3% NaCl solution, the fatigue strengths of both welds and base metal became lower than those in laboratory air due to the corrosive environment. However, the welds with Filler II had still the highest fatigue strengths compared with the base metal and welds with Filler I. It indicates that the addition of Al and Ti could suppress sensitization. In both welds, fatigue fracture took place at HAZ, and intergranular crack fractures were observed. It suggested that the heat input of welding led to the sensitization near HAZ.

著者関連情報
© 2018 社団法人 溶接学会
前の記事 次の記事
feedback
Top