内燃機関のアルミ製ピストン頭部に適用する遮熱のための溶射皮膜の特性評価
2014 年 65 巻 6 号 p. 276-282
詳細
2014 年 65 巻 6 号 p. 276-282
Properties of three thermal sprayed coatings were compared to select the effective sprayed coating for giving the thermal barrier to the Al alloy components of internal combustion engines. Results for coating 1 (top coat, Al2O3; bond coat, Ni-Cr), coating 2 (top coat, YSZ; bond coat, CoNiCrAlY), and coating 3 (SUS316) are presented below.
(1) After thermal cycle testing, no crack or delamination was apparent in coating 3.Partial cracks and delamination were observed in the top coating in coatings 1 and 2.
(2) All coatings have sufficient adhesion strength. The adhesion strength of coating 2 was especially high.
(3) The thermal barrier property of coating 2 was better than that of coating 1 or coating 3.
(4) Comprehensive evaluation results show that coating 2 had a good thermal barrier property and that coating 3 is a reasonable material because of its low cost as a thermal sprayed coating applied to Al alloy components of an internal combustion engine.