We examined the film composition stability of a Zn-Ni-SiO2 composite plating film under widely various current densities. Results demonstrated that the Zn-Ni-SiO2 composite plating film composition was stable over those conditions. Furthermore, results showed that the Zn-Ni-SiO2 film from the acidic chloride bath showed improvement over uniform deposition of Zn-Ni alloy plating. Our research results revealed that an agglomerated layer of SiO2 was formed near the Zn-Ni-SiO2 composite plating film surface, providing high corrosion resistance. Moreover, the silica-based thin layer coating on Zn-Ni-SiO2 composite plating film improved the corrosion resistance dramatically. Results demonstrated that adding SiO2 nanoparticles to Zn-Ni alloy plating baths improves functionality in acid chloride baths.