溶銑の脱りん速度に及ぼすCaF2添加量,温度,塩基度,生石灰粒径の影響
務川 進
著者情報
ジャーナル オープンアクセス HTML

2014 年 100 巻 4 号 p. 509-515

詳細
抄録

To clarify the optimum dephosphorization condition with CaF2 less fluxes, laboratory experiments were performed. The effect of CaF2 addition, CaO diameter, temperature and slag basicity on the rate of hot metal dephosphorization were evaluated. Addition of small amount of CaF2 drastically increased the rate of dephosphorization. This effect was attributed to the decrease in solid fraction of slag. At the conditions of the target basicity of 2.0 and using powder CaO, optimum temperature range was observed. At low temperature condition of 1270 °C, lower rate of dephosphorization was obtained. These phenomena are attributed to the loss of slag fluidity.

著者関連情報
© 2014 一般社団法人 日本鉄鋼協会

This article is licensed under a Creative Commons [Attribution-NonCommercial-NoDerivatives 4.0 International] license.
https://creativecommons.org/licenses/by-nc-nd/4.0/
前の記事 次の記事
feedback
Top