Nanostructural Analyses of Intra- and Intergranular Precipitates in High-temperature Heat-treated Nitrogen-added Austenitic Stainless Steel
Minoru OchiKousei SatoRyo TeranishiYukio SatoJun-ichi HamadaChikako TakushimaToru HaraKenji Kaneko
Author information
JOURNALS FREE ACCESS FULL-TEXT HTML

2019 Volume 105 Issue 4 Pages 418-425

Details
Abstract

More than one thousand intragranular and intergranular precipitates of nitrogen-added austenitic stainless steel, SUSXM15J1, were characterized by FIB-SEM serial-sectioning tomography, by conventional transmission electron microscopy (TEM) and by scanning transmission electron microscopy (STEM). All of intragranular precipitates were found nitrided to form dichromium nitride, Cr2N, Two types of intergranular precipitates were found Cr2N and Cr3Ni2Si(N), and some of them were grown and jointed due to the additional heat treatment during the tensile test at 1173 K. which probably contributed to its high-temperature strength.

Fullsize Image
Information related to the author
© 2019 The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top