ステンレス鋼に対する簡易浸炭処理法
森園 靖浩連川 貞弘山室 賢輝
著者情報
ジャーナル オープンアクセス

2012 年 98 巻 9 号 p. 476-481

詳細
抄録

A ferritic stainless steel was embedded in mixtures of steel and activated carbon powders, and heated at 1273 K for 3.6 ks in flowing N2. The specimen was quenched into the water after heating. This simplified treatment enabled the diffusion of carbon into the stainless steel, which is known to have difficulty in carburizing. The microstructural change was not recognized in the vicinity of the surface in the specimen heated in only activated carbon. However, the carburized layer was formed in the stainless steel when the steel powder was added to activated carbon. The thickness of the carburized layer was more than 200 μm in the case of the mixed powder consisting of 10 vol% steel powder and 90 vol% activated carbon, and increased with increasing steel powder. The surface hardness of the carburized steel also increased with increasing steel powder in the mixed powder. In addition, the carburized layer was observed in the stainless steel heated in mixtures of steel and graphite powders. The details of the carburization phenomenon are discussed on the basis of the measurement of carbon monoxide gas during heating and of the heat treatment without directly contacting with the mixed powder.

著者関連情報
© 2012 一般社団法人 日本鉄鋼協会

This article is licensed under a Creative Commons [Attribution-NonCommercial-NoDerivatives 4.0 International] license.
https://creativecommons.org/licenses/by-nc-nd/4.0/
前の記事 次の記事
feedback
Top