溶鉄中へのガス底吹きによる吸窒・脱窒速度
川上 正博伊藤 公允奥山 優菊池 拓三坂瀬 俊二
著者情報
ジャーナル フリー

1987 年 73 巻 6 号 p. 661-668

詳細
抄録

Argon and/or nitrogen was injected into molten pig iron through the bottom orifice.The experimental conditions are as follows : gas flow rate, 10-25Nl/min ; melt depth, 9-28cm temperature, 1400-1600°C.
The absorption rate from pure nitrogen was controlled by the mass transfer in metal phase.When Ar-N2 gas mixture was injected, however, the absorption rate was controlled by the mass transfer in gas phase.The desorption rate of nitrogen by pure argon was controlled by the gaseous mass transfer.
The volumetric rate constant, which is defined as the mass transfer coefficient multiplied by the total interfacial area between bubbles and molten iron, was obtained in different conditions.The rate constant for the gaseous mass transfer, Akg, increased linearly with the gas flow rate and the melt depth.The apparent activation energy was 64kcal/mol.The rate constant for the mass transfer in metal phase, Akm, increased proportionally to 0.65 power of the gas flow rate, and linearly with the melt depth.The apparent activation energy was 43kcal/mol.Akm/H obtained in the present work was compared with the published data, including not only those of nitrogen transfer, but also of oxygen transfer between bubbles and molten copper and silver.

著者関連情報
© 一般社団法人 日本鉄鋼協会
前の記事 次の記事
feedback
Top