ひずみ硬化指数を用いた延性き裂発生限界評価法
山田 剛久山下 洋一漢那 宗平
著者情報
ジャーナル フリー

2016 年 82 巻 842 号 p. 16-00096

詳細
抄録

Evaluation of ductile crack initiation limit without depending on materials was investigated. Ductile crack initiation behaviors were experimentally and analytically comprehended using Al alloy as non-ferrous metal in addition to two different steels. It was found that their limit characteristics were different between materials in the case of using conventional method based on stress triaxiality factor and equivalent plastic strain. It is considered that from cross section observations, ductile crack initiation for steels is caused by shear fracture between voids and the mechanism is different from Al alloy. Therefore, Mohr-Coulomb fracture criterion, which is related to normal stress and shear stress, was applied to the evaluation of steels. As a result, it was found that strain hardening exponent of the materials could be a new parameter. Using strain hardening exponent in addition to stress triaxiality factor and equivalent plastic strain, ductile crack initiation limit of different steels whose mechanism of ductile fracture is similar, can be evaluated with a master curve.

著者関連情報
© 2016 一般社団法人日本機械学会
前の記事 次の記事
feedback
Top