改良9Cr-1Mo鋼溶接継手のクリープ強度に及ぼす補修溶接の位置及び回数の影響

抄録

It is planned that Mod.9Cr-1Mo steel will be used as the structural material for the steam generator of the demonstration fast reactor. Creep strength of welded joints of Mod.9Cr-1Mo steel is lower than that of base metal at high temperature and long time. In addition, the creep strength of welded joints of Mod.9Cr-1Mo steel with repair welding is lower than that of without repair welding. In this study, the effects of the location and number of repair welds performed on the creep strength of welded joints of Mod.9Cr-1Mo steel were investigated, and a repair welding method was developed for the construction of the demonstration fast reactor. It was clarified that, regardless of the location and number of repair welds performed, the degradation in creep strength could be greatly reduced by performing the repair welding before post weld heat treatment (PWHT). Furthermore, it was found that the superposition of thermal history and the formation of a heat affected zone (HAZ) on the weld metal promote the coarsening of ferrite grains during creep and cause a slight reduction in creep strength. All repair welding was performed prior to PWHT, and a repair welding method was also developed to minimize thermal history superposition and weld metal HAZ formation.