The authors investigated the heat-treatment and mechanical properties of pearlitic malleable cast iron.
  On the heat-treatment the authors made dear that the heating rate of first stage graphitization has much influence on the structure, especialy on high silicon alloys, and when aboiding free ferrite in the structure may use faster than a certain heating rate.
  The temper carbon size was small when graphitized under the transformation temperature but large when graphitized over the transformation temperature.
  On the machanical properties the high temperature tensile strength and the wear resistance were investigated, and make clear that those properties were superior to plain gray cast iron. But the wear resistance was sensibly influenced by free ferrite.

View full abstract

  (1) Der Erfahrung, die erhält der Verfasser bei den Giessen der Dieselmotoren-Zylinder-Büchse d. h. zweitakl 233 Stücke und viertakt 584 Stücke, erwähnt. Die Ursache des Übels war untergesucht und richtige Giessweise, wie man darf giessen, war festgestellt.
  Abkühlungs geschwindigkeit und Perlitgefüge der Gussstücke im Innern des Querschnitts durch dre Überköpfe war bezeichnet.
  (2) Für grösser Büchse etwa 700 mm.φ u. 50 mm dick, kann man empfehlen C 2.8～3.2%, Si 0.8～1.2%, Mn 0.8～1.0%, und für feiner Büchse etwa 300 mm.φ u. 20 mm. dick, C 3.0～3.3%, Si 0.8～1.4%, Mn 0.6～0.9%.
  (3) Gussstücke von zweisortigen Eisen, eines von gewöhnlich Mn Gehalt und anders Mn 1.5%, war untergesucht und vergleicht durch die Radiographie. Man wird festigen, dass Mn Gehalt über 1% hat ungüngstigen Einfluss für Zylinderbüchse.

View full abstract